graphene_hybrid LaAlO3 hydrocarbon Oxide Alloy Vanadate Mechanical Formamidinium_lead_iodide BismuthVanadate YttriaStabilizedZirconia DiffractiveOpticalElements ring shape PANI Implant electrospinning IMT_Bucharest OpticalElement polyvinyl acetate HanyangUniv PolyStylene ScanningKelvinProbeMicroscopy Pores Pinpoint KPFM Current MagneticArray single_layer NUSNNI ContactModeDot Electrical&Electronics Optical Silver alkanes Molybdenum_disulfide IIT-chennai
Report image
If you found this image unacceptable, please let us know. We will review your report and take action if we determine this image is really unacceptable.
Calcium Hydroxyapatite Crystal growing
HA crystal grows according to the annealing time. From 24hrs, the crystal becomes clearly.
Scanning Conditions
- System: NX10
- Scan Mode: Non-contact
- Cantilever: AC160TS (k=26N/m, f=300kHz)
- Scan Size: 1μm×1μm
- Scan Rate: 0.17Hz
- Pixel: 512×256
- Scan Mode: Non-contact
- Cantilever: AC160TS (k=26N/m, f=300kHz)
- Scan Size: 1μm×1μm
- Scan Rate: 0.17Hz
- Pixel: 512×256